Description: High‐strength liquid epoxy with the necessary resiliency and strength to withstand forces generated by crushers and mills
Intended Use: Rod, ball, pebble, and autogenously mills; cone and gyratory crushers
Product features: 100% solids ‐ no solvents. High compression and impact strength. Negligible shrink. Easy to pour; easy to use. Low exothermic reaction.
1. Thoroughly clean the surface HOLDENBOND ® Conditioner to remove all oil, grease, and dirt.
2. Grit blast surface area with 8‐40 mesh grit, or grind with a coarse wheel or abrasive disc pad, to create increased surface area for better adhesion (Caution: An abrasive disc pad can only be used provided white mesh is revealed). Desired profile is 3‐5mil, including defined edges (do not ‘feather‐edge” epoxy).
Note: For metals exposed to sea water or other salt solution, grit‐blast and high‐pressure‐water‐blast the area, then leave overnight to allow any salts in the metal to “sweat” to the surface. Repeat blasting to “sweat out” all soluble salts. Perform chloride contamination test to determine soluble salt content (should be no more than 40ppm).
3. Clean surface again with HOLDENBOND ® conditioner to remove all traces of oil, grease, dust, or other foreign substances from the grit blasting.
4. Repair surface as soon as possible to eliminate any changes or surface contaminants.
WORKING CONDITIONS: Ideal application temperature is 55°F (12°C) to 90°F (32°C). In cold working conditions, heat repair area to 100‐110°F (37‐ 43°C) immediately prior to applying epoxy to dry off any moisture, contamination, or solvents, as well as to assist epoxy in achieving maximum adhesion properties.